粉末冶金轴承、化学成分和物理力学性能 (GB/T 2688—2012) |
|||||||||||||||
|
类别 |
合金成分 |
牌号 标记 |
化学成分/% |
物理力学性能 |
|||||||||||
|
Fe |
C化合 |
C总 |
Cu |
Sn |
Zn |
Pb |
其他 |
含油密度 /g·cm-3 |
含油率 /% |
径向压 溃强度 /MPa |
表观 硬度 HBS |
||||
|
铁
基 |
1 |
铁 |
FZ11060 FZ11065 |
余 |
＜0.25 |
＜0.5 |
— |
— |
— |
— |
＜2 |
＞5.6~6.0 ＞6.0~6.4 |
≥18 ≥12 |
≥200 ≥250 |
30~70 40~80 |
|
2 |
铁-石墨 |
FZ12058 FZ12062 |
余 |
0~0.5 |
2.0~3.5 |
— |
— |
— |
— |
＜2 |
＞5.6~6.0 ＞6.0~6.4 |
≥18 ≥12 |
≥170 ≥300 |
50~100 60~110 |
|
|
FZ12158 FZ12162 |
0.5~1.0 |
≥18 ≥12 |
≥310 ≥380 |
||||||||||||
|
3 |
铁-碳-铜 |
FZ13058 FZ13062 |
余 |
0~0.3 |
0~0.3 |
0~1.5 |
— |
— |
— |
＜2 |
＞5.6~6.0 ＞6.0~6.4 |
≥21 ≥17 |
≥100 ≥160 |
60~116 70~120 |
|
|
FZ13158 FZ13162 |
0.3~0.6 |
0.3~0.6 |
0~1.5 |
＞5.6~6.0 ＞6.0~6.4 |
≥21 ≥17 |
≥140 ≥190 |
|||||||||
|
FZ13258 FZ13262 |
0.6~0.9 |
0.6~0.9 |
0~1.5 |
＞5.6~6.0 ＞6.0~6.4 |
≥21 ≥17 |
≥140 ≥220 |
|||||||||
|
FZ13358 FZ13362 |
0.3~0.6 |
0.3~0.6 |
1.5~3.9 |
＞5.6~6.0 ＞6.0~6.4 |
≥21 ≥17 |
≥140 ≥240 |
|||||||||
|
FZ13458 FZ13462 |
0.6~0.9 |
0.6~0.9 |
1.5~3.9 |
＞5.6~6.0 ＞6.0~6.4 |
≥22 ≥17 |
≥170 ≥280 |
|||||||||
|
FZ13558 FZ13562 |
0.6~0.9 |
0.6~0.9 |
4~6 |
＞5.6~6.0 ＞6.0~6.4 |
≥22 ≥17 |
≥300 ≥320 |
|||||||||
|
FZ13658 FZ13662 |
0.6~0.9 |
0.6~0.9 |
18~22 |
＞5.6~6.0 ＞6.0~6.4 |
≥22 ≥17 |
≥300 ≥320 |
|||||||||
|
4 |
铁-铜 |
FZ14058 FZ14062 |
余 |
0~0.3 |
0~0.3 |
1.5~3.9 |
— |
— |
— |
＜3 |
＞5.6~6.0 ＞6.0~6.4 |
≥22 ≥17 |
≥300 ≥350 |
50~100 60~110 |
|
|
FZ14158 FZ14160 FZ14162 |
0~0.3 |
0~0.3 |
9~11 |
＞5.6~6.0 ＞6.0~6.4 ＞5.6~6.0 |
≥22 ≥19 ≥17 |
≥140 ≥210 ≥280 |
|||||||||
|
FZ14258 FZ14260 FZ14262 |
0~0.3 |
0~0.3 |
18~22 |
＞6.0~6.4 ＞5.6~6.0 ＞6.0~6.4 |
≥22 ≥19 ≥17 |
≥170 ≥210 ≥280 |
|||||||||
|
铜
基 |
1 |
铜-锡-锌-铅 |
FZ21070 FZ21075 |
＜0.5 |
— |
0.5~2.0 |
余 |
5~7 |
5~7 |
2~4 |
＜1.5 |
＞6.6~7.2 ＞7.2~7.8 |
≥18 ≥12 |
≥150 ≥200 |
20~50 30~60 |
|
2 |
铜-锡 |
FZ22062 FZ22066 FZ22070 FZ22074 |
— |
— |
0~0.3 |
余 |
9.5~10.5 |
— |
— |
＜2 |
＞6.0~6.4 ＞6.4~6.8 ＞6.8~7.2 ＞7.2~7.6 |
≥24 ≥19 ≥12 ≥9 |
＞130 ＞180 ＞260 ＞280 |
25~55 35~65 |
|
|
FZ22162 FZ22166 FZ22170 FZ22174 |
0.5~1.8 |
9.5~10.5 |
＞6.0~6.4 ＞6.4~6.8 ＞6.8~7.2 ＞7.2~7.6 |
≥22 ≥17 ≥9 ≥7 |
＞120 ＞160 ＞210 ＞230 |
||||||||||
|
FZ22260 FZ22264 |
2.5~5 |
6~10 |
＞5.8~6.2 ＞7.2~7.6 |
≥11 - |
＞70 ＞100 |
||||||||||
|
3 |
铜-锡-铅 |
FZ23065 |
＜0.5 |
— |
0.5~2.0 |
余 |
6~10 |
＜1 |
3~5 |
＜1 |
＞6.3~6.9 |
≥18 |
＞150 |
20~50 |
|
|
4 |
铜-锡-铁-碳 |
FZ24058 FZ24062 |
54.2~62 |
|
0.5~1.3 |
34~38 |
3.5~4.5 |
|
|
|
＞5.6~6.0 ＞6.0~6.4 |
≥22 ≥17 |
110~250 150~340 |
|
|
|
FZ24158 FZ24162 |
50.2~58 |
0.5~1.3 |
36~40 |
5.5~6.5 |
|
＞5.6~6.0 ＞6.0~6.4 |
≥22 ≥17 |
100~240 150~340 |
|||||||
|
FZ24258 FZ24262 FZ24266 |
余量 |
0~0.1 |
17~19 |
1.5~2.5 |
＜1 |
＞5.6~6.0 ＞6.0~6.4 ＞6.4~6.8 |
≥24 ≥19 ≥13 |
150 215 270 |
|||||||
|
注1.铁基各类轴承的化学成分中允许有＜1%的硫。 2. 化合碳含量允许用金相法评定。 3. 铜基各类轴承的化学成分中的总碳指游离石墨。 4. FZ24258、FZ24262、FZ24266系采用铁·青铜扩散合金化粉末的原料制作。 5.在同一个试件上三点硬度值的波动范围不许超过15个布氏单位。 6.材料牌号标记示例： 铁基1类含油密度为5.7~6.2g/cm3的粉末冶金轴承材料标记：
6.轴承成品应浸渍润滑油，一般用32号 L-AN 润滑油(GB/T 443—1989)浸渍，铁基轴承允许加入防锈剂。 |
|||||||||||||||