计算选型
|
一般用途耐热钢和合金铸件化学成分(GB/T8492—2002) |
|||||||||
|
牌 号 |
化 学 成 分(质 量 分 数)/% |
||||||||
|
C |
Si |
Mn |
P ≤ |
S ≤ |
Cr |
Mo ≤ |
Ni |
其他 |
|
|
ZG30Cr7Si2 |
0.20~0.35 |
1.0~2.5 |
0.5~1.0 |
0.04 |
0.04 |
6~8 |
0.5 |
≤0.5 |
— |
|
ZG40Cr13Si2 |
0.3~0.5 |
1.0~2.5 |
0.5~1.0 |
0.04 |
0.03 |
12~14 |
0.5 |
≤1 |
— |
|
ZG40Cr17Si2 |
0.3~0.5 |
1.0~2.5 |
0.5~1.0 |
0.04 |
0.03 |
16~19 |
0.5 |
≤1 |
— |
|
ZG40Cr24Si2 |
0.3~0.5 |
1.0~2.5 |
0.5~1.0 |
0.04 |
0.03 |
23~26 |
0.5 |
≤1 |
— |
|
ZG40Cr28Si2 |
0.3~0.5 |
1.0~2.5 |
0.5~1.0 |
0.04 |
0.03 |
27~30 |
0.5 |
≤1 |
— |
|
ZGCr29Si2 |
1.2~1.4 |
1.0~2.5 |
0.5~1.0 |
0.04 |
0.03 |
27~30 |
0.5 |
≤1 |
— |
|
ZG25Cr18Ni9Si2 |
0.15~0.35 |
1.0~2.5 |
≤2 |
0.04 |
0.03 |
17~19 |
0.5 |
8~10 |
— |
|
ZG25Cr20Ni14Si2 |
0.15~0.35 |
1.0~2.5 |
≤2 |
0.04 |
0.03 |
19~21 |
0.5 |
13~15 |
— |
|
ZG40Cr22Ni10Si2 |
0.3~0.5 |
1.0~2.5 |
≤2 |
0.04 |
0.03 |
21~23 |
0.5 |
9~11 |
— |
|
ZG40Cr24Ni24Si2Nb |
0.25~0.50 |
1.0~2.5 |
≤2 |
0.04 |
0.03 |
23~25 |
0.5 |
23~25 |
Nb1.2~1.8 |
|
ZG40Cr25Ni12Si2 |
0.3~0.5 |
1.0~2.5 |
≤2 |
0.04 |
0.03 |
24~27 |
0.5 |
11~14 |
— |
|
ZG40Cr25Ni20Si2 |
0.3~0.5 |
1.0~2.5 |
≤2 |
0.04 |
0.03 |
24~27 |
0.5 |
19~22 |
— |
|
ZG40Cr27Ni4Si2 |
0.3~0.5 |
1.0~2.5 |
≤1.5 |
0.04 |
0.03 |
25~28 |
0.5 |
3~6 |
— |
|
ZG45Cr20Co20Ni20Mo3W3 |
0.35~0.60 |
≤1.0 |
≤2 |
0.04 |
0.03 |
19~22 |
2.5~3.0 |
18~22 |
Co18~22 W2~3 |
|
ZG10Ni31Cr20Nb1 |
0.05~0.12 |
≤1.2 |
≤1.2 |
0.04 |
0.03 |
19~23 |
0.5 |
30~34 |
Nb0.8~1.5 |
|
ZG40Ni35Cr17Si2 |
0.3~0.5 |
1.0~2.5 |
≤2 |
0.04 |
0.03 |
16~18 |
0.5 |
34~36 |
— |
|
ZG40Ni35Cr26Si2 |
0.3~0.5 |
1.0~2.5 |
≤2 |
0.04 |
0.03 |
24~27 |
0.5 |
33~36 |
— |
|
ZG40Ni35Cr26Si2Nb1 |
0.3~0.5 |
1.0~2.5 |
≤2 |
0.04 |
0.03 |
24~27 |
0.5 |
33~36 |
Nb 0.8~1.8 |
|
ZG40Ni38Cr19Si2 |
0.3~0.5 |
1.0~2.5 |
≤2 |
0.04 |
0.03 |
18~21 |
0.5 |
36~39 |
|
|
ZG40Ni38Cr19Si2Nb1 |
0.3~0.5 |
1.0~2.5 |
≤2 |
0.04 |
0.03 |
18~21 |
0.5 |
36~39 |
Nb 1.2~1.8 |
|
ZNiCr28Fe17W5Si2C0.4 |
0.35~0.55 |
1.0~2.5 |
≤1.5 |
0.04 |
0.03 |
27~30 |
— |
47~50 |
W4~6 |
|
ZNiCr50Nb1C0.1 |
≤0.1 |
≤0.5 |
≤0.5 |
0.02 |
0.02 |
47~52 |
0.5 |
余量 |
N01.6 N+C0.2 Nb1.4~1.7 |
|
ZNiCr19Fe18Si1C0.5 |
0.4~0.6 |
0.5~2.0 |
≤1.5 |
0.04 |
0.03 |
16~21 |
0.5 |
50~55 |
— |
|
ZNiFe18Cr15Si1C0.5 |
0.35~0.65 |
≤2 |
≤1.3 |
0.04 |
0.03 |
13~19 |
— |
64~69 |
— |
|
ZNiCr25Fe20- Co15W5Si1C0.46 |
0.44~0.48 |
1~2 |
≤2 |
0.04 |
0.03 |
24~26 |
— |
33~37 |
W4~6 Co14~16 |
|
ZCoCr28Fe18C0.3 |
≤0.5 |
≤1 |
≤1 |
0.04 |
0.03 |
25~30 |
0.5 |
1 |
Co48~52 Fe20最大值 |
|
注：GB/T 8492—2002《一般用途耐热钢和合金铸件》包括的牌号，代表了适合在一般工程中不同耐热条件下广泛应用的铸造耐热钢和耐热合金铸件的种类。如果要求采用GB/T 8492—2002未规定的牌号，则应在订货合同中注明。 |
|||||||||